Multilaminati piezoelettrici a gradiente funzionale

Mercadelli, Elisa (2010) Multilaminati piezoelettrici a gradiente funzionale, [Dissertation thesis], Alma Mater Studiorum Università di Bologna. Dottorato di ricerca in Chimica industriale, 22 Ciclo. DOI 10.6092/unibo/amsdottorato/2822.
Documenti full-text disponibili:
[img]
Anteprima
Documento PDF (Italiano) - Richiede un lettore di PDF come Xpdf o Adobe Acrobat Reader
Download (8MB) | Anteprima

Abstract

Aim of this thesis was the production of porosity-graded piezoelectric ceramics for ultrasonic applications by tape casting and screen printing. The study and optimization of each single step of the tape casting process allowed to produce flat and crack-free multilayers of Pb0.988(Zr0.52Ti0.48)0.976Nb0.024O3 (PZTN) of uniform and graded porosity. The multilayers of thickness ranging between 400 and 800 µm were produced stacking optimized green layers with different amount of pore former. The functionally graded materials showed porosity ranging between 10 and 30% with piezoelectric properties suitable for the specific ultrasonic applications. Screen printing inks of PZTN for deposition onto four different substrates were studied and optimized. Thick films with thickness ranging between 4 and 20 µm were produced tailoring the screen printing parameters and number of depositions.

Abstract
Tipologia del documento
Tesi di dottorato
Autore
Mercadelli, Elisa
Supervisore
Co-supervisore
Dottorato di ricerca
Scuola di dottorato
Scienze chimiche
Ciclo
22
Coordinatore
Settore disciplinare
Settore concorsuale
Parole chiave
Ceramici Piezoelettrici PZTN Porosità Gradiente Multilaminati
URN:NBN
DOI
10.6092/unibo/amsdottorato/2822
Data di discussione
29 Marzo 2010
URI

Altri metadati

Statistica sui download

Gestione del documento: Visualizza la tesi

^